紗股在不經扭撚下併股成束, 適用於噴佈成型法, 預混法（片式熟料, 糰式熟料）, 生產需要切段式加工之製品, 或中低纖維含量之加工品
產品規格
物性規格範圍
包裝方式 |
|
|
| |
|
| |
| 回到上面 |
|
| 產品規格 |
| |
|
| |
產品編號 |
|
漿料編號 |
|
加工方式 |
|
適用樹脂 |
|
TEX No.
(g/km) |
|
| |
TGFR |
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
| |
G2300 |
|
357B |
|
Spray-up |
|
聚酯樹脂 |
|
2300 |
|
| |
|
|
|
|
|
|
|
|
|
|
| |
G4800 |
|
357B |
|
Spray-up |
|
聚酯樹脂 |
|
4800 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
| |
產品編號 |
|
漿料編號 |
|
加工方式 |
|
適用樹脂 |
|
TEX No.
(g/km) |
|
| |
TGFR |
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
| |
S2200-S
|
|
433(S1)
905B(S2)
(Soft type)
|
|
S.M.C |
|
聚酯樹脂
乙烯酯樹脂 |
|
2200 |
|
| |
|
|
|
|
|
|
|
|
|
|
| |
S4400-S
|
|
433(S1)
905B(S2)
(Soft type) |
|
S.M.C |
|
聚酯樹脂
乙烯酯樹脂 |
|
4400 |
|
| |
|
|
|
|
|
|
|
|
|
|
| |
S2200-M
|
|
973
(Middle type) |
|
S.M.C |
|
聚酯樹脂
乙烯酯樹脂 |
|
2200 |
|
| |
|
|
|
|
|
|
|
|
|
|
| |
S4400-M
|
|
973
(Middle type) |
|
S.M.C |
|
聚酯樹脂
乙烯酯樹脂 |
|
4400 |
|
| |
|
|
|
|
|
|
|
|
|
|
| |
L2400 |
|
992 |
|
Laminating
(Panel) |
|
聚酯樹脂 |
|
2400 |
|
| |
|
|
|
|
|
|
|
|
|
|
| |
L4400 |
|
992 |
|
Laminating
(Panel) |
|
聚酯樹脂 |
|
4400 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
| |
|
| 回到上面 |
|
| 物性規格範圍 |
| |
|
| |
產品編號 |
|
TEX(g/km)
|
|
燒失量(％) |
|
分紗股數(股) |
|
水份(％) |
|
單纖直徑
µm |
|
| |
TGFR |
|
中心值 |
|
中心值 |
|
中心值 |
|
|
|
|
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
G2300 |
|
2300 |
|
1.10 |
|
35 |
|
<0.05 |
|
11 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
G4800 |
|
4800 |
|
1.10 |
|
74 |
|
<0.05 |
|
11 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
S2200-S1 |
|
2200 |
|
1.80 |
|
28 |
|
<0.08 |
|
13 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
S4400-S1 |
|
4400 |
|
1.80 |
|
56 |
|
<0.08 |
|
13 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
S4400-S2 |
|
4400 |
|
1.10 |
|
56 |
|
<0.08 |
|
13 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
S2200-M |
|
2200 |
|
1.85 |
|
28 |
|
<0.08 |
|
13 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
S4400-M
|
|
4400 |
|
1.85 |
|
56 |
|
<0.08 |
|
13 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
L2400 |
|
2400 |
|
0.70 |
|
66 |
|
<0.08 |
|
11 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
| |
L4400 |
|
4400 |
|
0.70 |
|
122 |
|
<0.08 |
|
11 |
|
| |
|
|
|
|
|
|
|
|
|
|
|
|
|
|
|
| |
|
|
|
|
|