| Feature： |
| |
|
‧Random-directional property. High affinity to thicker laminates at lower cost.
‧Unified directional character of the mechanical property form the laminates.
‧Higher content of resin. Better impregnation.
‧Excellent bonding effects amount laminates.
‧Mats of non-continuous chopped strands have smaller damaged area of laminates upon impact.
‧Better finishing surface processing of the laminates.
‧E-Tpye: Excellent surface bonding efficiency. Working environment can be improved to low pollution
and better operation conditions for working people.
‧P-Type: The laminates have better transparency.
|
| |
| |
| Certificate： |
| |
.gif) |
 |
 |
| Lloyd’s Register of Shipping |
Det Norske Veritas |
China Corporation Register of Shipping |
|
| |
| |
| |
| Products and Applications： |
| |
| Product |
Product Characteristic |
Resin System |
Example of End-Product Application |
| Powder type |
Fast wet out, great performance in laminate transparency |
U.P./V.E. |
Exterior of automobile and marine vehicles, Tanks, Corrugated sheets |
| Emulsion type *1 |
Lower spreading out of glassfiber strands in the operating environment |
|
| *1 Emulsion bonded mat includes hard type, middle type and soft type. |
| |
| |
| Significant Physical Properties： |
| |
| Product |
Basic Weight *1
(Nom. ± Variation)
(g/m2) |
L.O.I.
(%)
|
Moisture Content
(% max) |
| 80P |
80 ± 8 |
14.0 ± 4.0 |
< 0.20 |
| 90P |
90 ± 9 |
12.0 ± 4.0 |
| 100P |
100 ± 10 |
9.0 ± 4.0 |
| 110P |
110 ± 11 |
| 150P |
150 ± 15 |
| 230P |
230 ± 23 |
5.0 ± 2.0 |
| 270P |
270 ± 27 |
5.0 ± 2.0 |
| 300P |
300 ± 30 |
4.5 ± 1.8 |
| 450P |
450 ± 45 |
3.0 ± 1.2 |
| 600P |
600 ± 60 |
| 100E |
100 ± 10 |
6.0 ± 4.0 |
| 110E |
110 ± 11 |
| 150E |
150 ± 15 |
| 230E |
230 ± 23 |
5.0 ± 2.0 |
| 270E |
270 ± 27 |
4.5 ± 1.2 |
| 300E |
300 ± 30 |
4.2 ± 1.2 |
| 450E |
450 ± 45 |
4.0 ± 1.2 |
| 600E |
600 ± 60 |
3.5 ± 0.9 |
|
| *1 Production range : basic weight 220g/m2 ~ 900g/m2 ; width 200mm ~ 2600mm. |
| |
| |
|
Product
|
1040mm width |
1210mm width |
1860mm width |
Length
(M/ROLL) |
Weight
(KG/ROLL) |
Length
(M/ROLL) |
Weight
(KG/ROLL) |
Length
(M/ROLL) |
Weight
(KG/ROLL) |
|
230P/E
|
125 |
30 |
144 |
40 |
117 |
50 |
| 270P/E |
107 |
122 |
100 |
| 300P/E |
96 |
110 |
90 |
| 450P/E |
64 |
73 |
60 |
| 600P/E |
48 |
55 |
45 |
|
| |
| |
| Packaging & Palletizing： |
| |
Width
(mm) |
Carton/Pallet*1 |
Carton dimension
L x W x H (mm) |
Package dimension*2
L x W x H (mm) |
| 1040 |
12 |
1100 x 275 x 275 |
1140 x 1140 x 945 |
| 16 |
1140 x 1140 x 1220 |
| 1210 |
12 |
1260 x 315 x 315 |
1290 x 970 x 1410 |
| 18 |
1290 x 970 x 2060 |
| 1860 |
12 |
1950 x 275 x 275 |
1950 x 1140 x 950 |
| 16 |
1140 x 1140 x 2100 |
Carton dimension
|
| |
|
*1 Each mat is packaged in protective PE bag within a carton.
*2 Package dimension contains pallet stature. |
| |
| Storage Conditions： |
| |
|
Store Chopped Strand Mat in a cool, dry area. Suitable temperature : 21±11℃ , R.H. : 60±20％. (Temperature should not exceed 35℃ & R.H. should be kept below 75％ is also recommended). It is recommended to bring material in the working place 24 hours at least prior to use. Do not stack higher than two pallets.
|
| |
| |
|
Examples of Applications ：
|
| |
| Glass fiber is an inorganic fiber completely incombustible. Glass fiber has excellent electrical insulation properties, high tensile strength in relation to weight and dimensional stability, good weather and corrosion resistance. Glass fiber is an excellent reinforcement material, has low cost, high strength-to–weight ratio advantages comparing to aluminum or other metals. |
|
.jpg)
|
| 18 cartons of 1210mm CSM |
| |
|
| Chopped Strand Mat suits Hand Lay-Ups for molding objects of low curvatures, of small quantity, or objects require good finishing surface. It is typically used to make corrugated sheets, flat sheets, boats, vehicle components, bath tubs, containers, water tanks, tables and chairs, etc. Application includes transportation, aerospace, marine, housing and construction, industrial/public facilities, sports/recreation, etc. |
| |
| |